Archive for the “Chemical Processing” Category


Cracking Of Stainless Steel Nozzle Sleeve

Posted on April 6th, 2016 by Met-Tech

Share This Case Study:

Fatigue Cracking Of A 316l Stainless Steel Nozzle Sleeve From A Chemical Processing Vessel Corrosion Assisted Fatigue Cracking Of A 316l Stainless Steel Nozzle Sleeve From A Chemical Processing Vessel Summary: A cracked nozzle sleeve stub from XXXX Vessel of the proprietary vaporizer system was analyzed to determine the cause of cracking. Results indicate axial […]


Cracked Nitrided Tool Steel Die Plate

Posted on September 27th, 2018 by Met-Tech

Share This Case Study:

  Failure Analysis of Fractured Tool Steel Die Plate Summary: A cracked polymer filament die plate was received for analysis to determine the cause of cracking. Results indicate the die plate cracked as a result of a brittle nitrided case and an insufficient cross-sectional area of the narrow ligament between the cap screw hole and […]

Tags: , , , , ,


Cracked Impeller Blade

Posted on April 6th, 2016 by Met-Tech

Share This Case Study:

Failure Analysis of Cracked Impeller Blades SUMMARY: Two blade samples of a cracked ******************* centrifugal blower impeller blade was submitted for metallurgical analysis of the cracks. The cracks in the submitted blade samples were found to have initiated at corrosion pits on the leading edge of the blades. Initial propagation was by stress corrosion cracking […]

img23

Failure Analysis Services

Determine cause of failure & recommend ways to prevent future recurrence.

View more
img23

Corrosion Investigation

Determine cause of material degradation that reduces life expectancy.

View more
img23

SEM/EDS
Micro-Analysis

Verify fracture mechanism & initiation. Microstructure composition and imaging.

View more
img23

Metallography Services

Reveals grain structure, thermo mechanical processing & flaw and defect characteristics.

View more