Corrosion Of A Leaking Marine Oil Cooler

Posted on August 7th, 2017 by Met-Tech

Share This Case Study:

Analysis Of Condensate Induced Pitting Corrosion Of A Leaking Marine Oil Cooler Summary: Two cores from a marine diesel engine oil cooler were received for analysis to investigate the cause of failure via leaking. Results indicate that the cooler core failed due to pitting corrosion initiated on the interior (oil side) at the edge of […]